ທໍ່ສະແຕນເລດ 304L ASME SA213 TP304L ASTM A213 TP304L

ທໍ່ເຫຼັກສະແຕນເລດ ASTM A269 304L, ທໍ່ເຫຼັກບິດ ASTM A213 SA213 TP304L, ທໍ່ເຫຼັກສະແຕນເລດ ASTM A312 SA312 TP 316L, ທໍ່ເຫລໍກສະແຕນເລດ 304L, ທໍ່ ASTM A213 SA213 304L U, ທໍ່ເຫຼັກສະແຕນເລດ EN 10216-5 1.4307 ໃນປະເທດຈີນ. ທໍ່ ASTM A312 SA312 TP 316L, ທໍ່ເຫລໍກສະແຕນເລດ 304L, ທໍ່ ASTM A213 SA213 304L U ໂຄ້ງ, ທໍ່ EN 10216-5 1.4307 ໃນປະເທດຈີນ. ທໍ່ 304L ສະແຕນເລດ.

ເສັ້ນຜ່າກາງພາຍນອກ: 6 - 530 ມມ
ຄວາມຫນາຂອງກໍາແພງ: 0.50 - 64 ມມ

ສະເພາະມາດຕະຖານ:
EN 10216-5; DIN 17456, DIN 17458, DIN 2462, DIN 17455
GB / T14975; T14976; T13296; GB5310;
ASTM A213, A269, A312, A511, A789, A790, A928, A999, A1016, ASTM B161, ASTM B163, ASTM B165, ASTM B167, ASTM B338, ASTM B407, ASTM B423, ASTM B444, ASTM B164, ASTM B166, ASTM B164, ASTM B164, ASTM B164, ASTM B164, B626, ASTM B668, ASTM B677, ASTM B829
JIS G3459, JIS G3463, JIS G3446, JIS G3447, JIS G3448, JIS G3468
GOST 9940; GOST 9941;

ການປະສົມສານເຄມີ:

ຊັ້ນ	-	ຄ	ມ	Si	ພ	ສ	ປ	ມ	ນ	ນ
304L / S30403	min.max.	-0.035	-2	-1	-0.045	-0.03	18.0-20.0	-	8.0-12.0	-
304 / S30400	min.max.	-0.08	-2	-1	-0.045	-0.03	18.0-20.0	-	8.0-11.0	-
EN 10216-5 1.4301	min.max.	-0.07	-2	-1	-0.04	-0.015	17.00-19.5	-	8.0-10.5	-0.11
EN 10216-5 1.4307	min.max.	-0.03	-2	-1	-0.04	-0.015	17.5-19.5	-	8.0-10.0	-0.11
304H / S30409	min.max.	0.04-0.10	-2	-1	-0.045	-0.03	18.0-20.0	-	8.0-11.0	-
EN 10216-5 1.4948	min.max.	0.04-0.08	-2	-1	-0.035	-0.015	17.0-19.0	-	8.0-11.0	-0.11

ຄຸນສົມບັດກົນຈັກ:

-	ຄວາມເຂັ້ມແຂງ Tensile	ຄວາມເຂັ້ມແຂງຂອງຜົນຜະລິດ	ຍືດຍາວ	ຄວາມແຂງກະດ້າງ	ຄວາມແຂງກະດ້າງ
ຊັ້ນ	(MPa) ນາທີ	0.2% ຫຼັກຖານສະແດງ (MPa)	(% ໃນ 50 ມມ) ນາທີ	ສູງສຸດຂອງ Rockwell B (HR B)	Brinell (HB) ສູງສຸດ
304L	485	170	35	90	192
304	515	205	35	90	192
304H	515	205	35	90	192

ຄຸນສົມບັດທາງກາຍະພາບ:

ຄວາມຫນາແຫນ້ນຂອງທໍ່ສະແຕນເລດ 304L (lb / cu. in.)	0.29
ແຮງໂນ້ມຖ່ວງສະເພາະ (g / cm³)	7.93
ຄວາມຮ້ອນສະເພາະ (Btu / lb / Deg ° F - [32-212 ອົງສາ° F])	0.12
ຄວາມຕ້ານທານໄຟຟ້າ (microhm-cm (ຢູ່ທີ່ 68 ອົງສາ F)	432
ຈຸດລະລາຍ (ປະລິນຍາ° F)	2650
ແບບໂມດູນຂອງຄວາມເຄັ່ງຕຶງທາງດ້ານຮູບແບບ	28